Integrated Optical Fiber and Epsilon-Near-Zero Material

ABSTRACT

The present disclosure provides an optical waveguide design of a fiber modified with a thin layer of epsilon-near-zero (ENZ) material. The design results in an excitation of a highly confined waveguide mode in the fiber near the wavelength where permittivity of thin layer approaches zero. Due to the high field confinement within thin layer, the ENZ mode can be characterized by a peak in modal loss of the hybrid waveguide. Results show that such in-fiber excitation of ENZ mode is due to the coupling of the guided fundamental core mode to the thin-film ENZ mode. The phase matching wavelength, where the coupling takes place, varies depending on the refractive index of the constituents. These ENZ nanostructured optical fibers have many potential applications, for example, in ENZ nonlinear and magneto-optics, as in-fiber wavelength-dependent filters, and as subwavelength fluid channel for optical and bio-photonic sensing.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Ser. No. 62/800,806, filed Feb. 4, 2019, entitled “Integrated Optical Fiber and Epsilon-Near-Zero Material”, which is incorporated herein by reference.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

Not applicable.

REFERENCE TO APPENDIX

Not applicable.

BACKGROUND OF THE INVENTION Field of the Invention

The disclosure generally relates to optical fiber. More specifically, the disclosure relates to optical fiber integrated with epsilon-near-zero capable materials that affects the performance characteristics of the optical fiber.

Description of the Related Art

Optical response of near-zero refractive index systems has been a topic of interest recently as the electromagnetic field inside the media with near-zero parameters, such as vanishing permittivity and permeability values, have been shown to exhibit unique optical properties. Those features may be exploited in various optical applications such as wavefront engineering, radiation pattern tailoring, non-reciprocal magneto-optical effects, nonlinear ultrafast optical switching, dielectric permittivity sensing, and broadband perfect absorption. Recent studies suggest that epsilon-near-zero (ENZ) properties can also be observed in a single highly doped conducting oxide thin film. Materials having ENZ properties include materials with low permittivity. Unique properties observed include enhanced absorption in transparent conducting oxide (TCO) ENZ layers, advanced resonant coupling properties with antenna, and strongly enhanced nonlinear response and light generation in a TCO slab. In addition, electrical tuning of conducting oxide materials to the ENZ regime results in efficient light manipulation and modulation. However, most of the studies on ENZ optical properties are limited to the excitation of ENZ mode in the planar structures or meta-surfaces with short interaction length, restricting the excitation platform.

Optical fiber is well-known example of a way to guide and manipulate light. It has been used extensively in various applications including long distance optical communication, light generation using fiber lasers, remote and optical sensing, fiber imaging in endoscopes, and fiber laser surgery. Although a dielectric optical waveguide is very efficient in transmitting light, its functionality is somewhat limited by the dielectric material of the core, which has poor electronic, magneto-optical, and nonlinear-optical responses and has the dielectric diffraction limit. Therefore, the optical properties of the optical fiber waveguide such as phase, amplitude, polarization state, and mode profile cannot be altered after the fiber drawing fabrication.

Therefore, there is a need to integrate new materials and nanostructures into fiber components for enhanced processing and transmission capabilities and novel functionalities.

BRIEF SUMMARY OF THE INVENTION

The present disclosure provides an optical waveguide design of a fiber modified with a thin layer of epsilon-near-zero (ENZ) material. The design results in an excitation of a highly confined waveguide mode in the fiber near the wavelength where permittivity of thin layer approaches zero. Due to the high field confinement within thin layer, the ENZ mode can be characterized by a peak in modal loss of the hybrid waveguide. Results show that such in-fiber excitation of ENZ mode is due to the coupling of the guided fundamental core mode to the thin-film ENZ mode. The phase matching wavelength, where the coupling takes place, varies depending on the refractive index of the constituents. These ENZ nanostructured optical fibers have many potential applications, for example, in ENZ nonlinear and magneto-optics, as in-fiber wavelength-dependent filters, and as subwavelength fluid channel for optical and bio-photonic sensing. Propagating fields can be confined inside a conducting oxide/metal nitride ENZ materials embedded in an optical fiber waveguide. Examples of optical fibers include a nanobore fiber, an anti-resonance hollow core optical fiber, and an optical fiber with D-shaped platform.

In general, the disclosure provides an optical fiber, an optical fiber coupled with a layer of transparent conducting oxide, a method of manufacturing an optical fiber, and a method of using an optical fiber, as disclosed and discussed herein.

The disclosure provides an optical fiber, comprising: a longitudinal core layer of dielectric material; a longitudinal cladding layer surrounding at least a portion of the core; and a longitudinal layer of ENZ material formed parallel to the core.

The disclosure also provides an optical fiber, comprising: a longitudinal hollow core; a longitudinal cladding layer surrounding at least a portion of the core; and a longitudinal layer of ENZ material formed parallel to the core.

The disclosure further provides a method of alternating light in an optical fiber, the optical fiber having a longitudinal core layer of dielectric material, a longitudinal cladding layer surrounding at least a portion of the core, and a longitudinal layer of ENZ material formed parallel to the core, the method comprising: providing light to the optical fiber; and absorbing at least a portion of the light along the core as a result of the ENZ layer.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

The patent or application file contains at least one drawing executed in color. Copies of this patent or patent application publication with color drawing(s) will be provided by the Office upon request and payment of the necessary fee.

FIG. 1A is schematic of an example of an embodiment of an ENZ optical fiber waveguide design with two inserts of expanded cross sections of portions of a core with an ENZ coating and without an ENZ coating as indicated.

FIG. 1A′ is a schematic graph of transmission of a light through the optical fiber of FIG. 1A, based on wavelength.

FIG. 1B is a schematic model of an example of an ENZ coating on a doped core surface for excitation of an ENZ thin film mode.

FIG. 1B′ is a schematic graph of absorption of a light through the model of FIG. 1B, based on wavelength.

FIG. 2A is a schematic contour plot of reflectance as a function of wavelength and incident angle for a glass-ITO-ethanol as an example of a thin-film ENZ mode of a three-layer structure shown in the insert of FIG. 2D (as a model of the Section (II) of FIG. 1A).

FIG. 2B is a schematic contour plot of reflectance as a function of wavelength and incident angle for a glass-ITO-air as an example of a thin-film ENZ mode of a three-layer structure.

FIG. 2C is a schematic contour plot of reflectance as a function of wavelength and incident angle for a glass-ITO-acetonitrile as an example of a thin-film ENZ mode of a three-layer structure.

FIG. 2D is a schematic graph of field intensity (|E|) as a function of depth inside the ITO layer for the examples of structures in FIGS. 2A-2C.

FIG. 3 is a schematic graph of phase matching conditions between fundamental waveguide modes in a hollow nanobore fiber and thin-film ENZ modes of a glass-ITO-air three-layer geometry with ITO layer thicknesses of 5 nm, 10 nm, 15 nm, and 20 nm.

FIG. 4A is a schematic electric field profile of the fundamental mode supported by the ENZ optical fiber at a 900 nm outside ENZ wavelength, the profile being across the entire fiber cross section in the top image with a zoomed schematic view of the core below the top image.

FIG. 4B is a schematic electric field profile of the fundamental mode supported by the ENZ optical fiber at a 1080 nm outside ENZ wavelength, the profile being across the entire fiber cross section in the top image with a zoomed schematic view of the core below the top image.

FIG. 4C is a schematic electric field profile of the fundamental mode supported by the ENZ optical fiber at a 1300 nm outside ENZ wavelength, the profile being across the entire fiber cross section in the top image with a zoomed schematic view of the core below the top image.

FIG. 4D is a schematic graph of the electric field along the diameter of the fiber in FIG. 4A at the 900 nm outside ENZ wavelength.

FIG. 4E is a schematic graph of the electric field along the diameter of the fiber in FIG. 4B at the 1000 nm outside ENZ wavelength.

FIG. 4F is a schematic graph of the electric field along the diameter of the fiber in FIG. 4C at the 1300 nm outside ENZ wavelength.

FIG. 5 is a schematic graph of modal losses of ENZ fiber higher order modes.

FIG. 6A is a schematic graph of a complex refractive index of ITO as a function of free space wavelength.

FIG. 6B is a schematic graph of permittivity of ITO as a function of free space wavelength. At the crossover of real and imaginary parts of the index, the real part of permittivity vanishes.

FIG. 7A is a schematic graph of refractive index dependence of the ENZ fiber based on various analytes placed inside the core channel of the fiber.

FIG. 7B is a schematic graph of a refractive index dependence of ENZ resonance wavelength.

FIG. 7C is a schematic graph of a refractive index dependence of loss.

FIG. 8A is a schematic electric field profile at ENZ resonance for air as an analyte placed inside the core of an ENZ optical fiber with an ITO shell in the core, the profile being across the entire fiber cross section in the top image with an expanded schematic view of the core below the top image.

FIG. 8B is a schematic electric field profile at ENZ resonance for chloroform as an analyte placed inside the core of an ENZ optical fiber with an ITO shell in the core, the profile being across the entire fiber cross section in the top image with an expanded schematic view of the core below the top image.

FIG. 8C is a schematic graph of the electric field along the diameter of the fiber in FIG. 8A.

FIG. 8D is a schematic graph of the electric field along the diameter of the fiber in FIG. 8B.

FIG. 9A is a schematic diagram of an example of a conducting oxide field-effect structure used in light manipulation.

FIG. 9B is a schematic graph of a spatial distribution of the carrier concentration N for different applied voltages using the structure of FIG. 9A.

FIG. 9C is a schematic graph of a corresponding real part of the dielectric permittivity of ITO at wavelength of 1550 nm.

FIG. 10A is a schematic diagram of an example of a nanobore fiber used for excitation of ENZ resonance.

FIG. 10B is a SEM image of a nanobore of the fiber of FIG. 10A showing an AZO coating in the hollow channel of the nanobore as an exemplary ENZ material.

FIG. 10C is a schematic electric field profile of the fundamental mode supported by the ENZ optical fiber of FIG. 10A at a 900 nm outside ENZ wavelength.

FIG. 11A is a schematic diagram image of an example of another embodiment of an ENZ hollow core fiber with thin tubes around the periphery of a hollow core, the fiber having anti-resonance properties.

FIG. 11B is a schematic enlarged diagram of the hollow core of the anti-resonance ENZ hollow core fiber in FIG. 11A.

FIG. 11C is a SEM of an example of TCO (AZO) nanoparticles deposited into the hollow core 8′.

FIG. 11D is a schematic graph of measured transmission spectra for the anti-resonance fiber filled with the AZO nanoparticles with different doping concentrations.

FIG. 11E is a schematic diagram of a hollow core photonic crystal fiber as an example of tubes outside the hollow core that can be used for anti-resonance properties.

FIG. 11F is a schematic enlarged diagram of the hollow core with the surrounding tubes of the ENZ hollow core photonic crystal fiber in FIG. 11E.

FIG. 12A is a schematic diagram of another embodiment of an ENZ fiber having an ENZ coating external to the core.

FIG. 12B is a schematic graph of a real part of permittivity dispersion of deposited AZO thin film with an ENZ wavelength of about 1580 nm.

FIG. 12C is a schematic graph of a measured transmission spectrum of AZO ENZ materials on the ENZ fiber of FIG. 12A.

FIG. 12D is a schematic diagram showing a mode profile of the ENZ fiber of FIG. 12A at a resonance wavelength.

FIG. 12E is a schematic diagram showing an enlarged y-component of electrical field distribution for TE incident light for the ENZ fiber of FIG. 12A.

FIG. 12F is a schematic diagram showing an enlarged y-component of electrical field distribution for TM incident light for the ENZ fiber of FIG. 12A.

FIG. 12G is a schematic diagram showing a line profile of the y-component electrical field distribution along a diameter of the ENZ fiber of FIG. 12A with TM incident light at a resonance wavelength.

FIG. 13A is a schematic diagram of another embodiment of an ENZ fiber having an ENZ coating with magneto-optical properties.

FIG. 13B is a schematic diagram of polarized input light being reoriented by magnetic field through the ENZ coating in the ENZ fiber of FIG. 13A.

FIG. 13C is an example of a system to reorient and measure a polarized light through the ENZ fiber of FIG. 13A.

FIG. 14A is a schematic diagram of another embodiment of an ENZ fiber having a tunable ENZ coating external to the core.

FIG. 14B is a schematic graph of a change of the loss from 0V to 5V for various wavelengths of the ENZ fiber of FIG. 14A.

FIG. 14C is a schematic diagram of a carrier concentration profile of the ITO layer for the ENZ fiber of FIG. 14A without an applied voltage.

FIG. 14D is a schematic diagram of a carrier concentration profile of the ITO layer for the ENZ fiber of FIG. 14A with an applied voltage of 3 V.

DETAILED DESCRIPTION

The Figures described above and the written description of specific structures and functions below are not presented to limit the scope of what Applicant has invented or the scope of the appended claims. Rather, the Figures and written description are provided to teach any person skilled in the art to make and use the inventions for which patent protection is sought. Those skilled in the art will appreciate that not all features of a commercial embodiment of the inventions are described or shown for the sake of clarity and understanding. Persons of skill in this art will also appreciate that the development of an actual commercial embodiment incorporating aspects of the present disclosure will require numerous implementation-specific decisions to achieve the developer's ultimate goal for the commercial embodiment. Such implementation-specific decisions may include, and likely are not limited to, compliance with system-related, business-related, government-related, and other constraints, which may vary by specific implementation or location, or with time. While a developer's efforts might be complex and time-consuming in an absolute sense, such efforts would be, nevertheless, a routine undertaking for those of ordinary skill in this art having benefit of this disclosure. It must be understood that the inventions disclosed and taught herein are susceptible to numerous and various modifications and alternative forms. The use of a singular term, such as, but not limited to, “a,” is not intended as limiting of the number of items. Further, the various methods and embodiments of the system can be included in combination with each other to produce variations of the disclosed methods and embodiments. Discussion of singular elements can include plural elements and vice-versa. References to at least one item may include one or more items. Also, various aspects of the embodiments could be used in conjunction with each other to accomplish the understood goals of the disclosure. Unless the context requires otherwise, the term “comprise” or variations such as “comprises” or “comprising,” should be understood to imply the inclusion of at least the stated element or step or group of elements or steps or equivalents thereof, and not the exclusion of a greater numerical quantity or any other element or step or group of elements or steps or equivalents thereof. The device or system may be used in a number of directions and orientations. The order of steps can occur in a variety of sequences unless otherwise specifically limited. The various steps described herein can be combined with other steps, interlineated with the stated steps, and/or split into multiple steps. Some elements are nominated by a device name for simplicity and would be understood to include a system or a section, such as a processor would encompass a processing system of related components that are known to those with ordinary skill in the art and may not be specifically described.

The present disclosure provides an optical waveguide design of a fiber modified with a thin layer of epsilon-near-zero (ENZ) material. The design results in an excitation of a highly confined waveguide mode in the fiber near the wavelength where permittivity of thin layer approaches zero. Due to the high field confinement within thin layer, the ENZ mode can be characterized by a peak in modal loss of the hybrid waveguide. Results show that such in-fiber excitation of ENZ mode is due to the coupling of the guided fundamental core mode to the thin-film ENZ mode. The phase matching wavelength, where the coupling takes place, varies depending on the refractive index of the constituents. These ENZ nanostructured optical fibers have many potential applications, for example, in ENZ nonlinear and magneto-optics, as in-fiber wavelength-dependent filters, and as subwavelength fluid channel for optical and bio-photonic sensing. Propagating fields can be confined inside a conducting oxide/metal nitride ENZ materials embedded in an optical fiber waveguide. Examples of optical fibers include a nanobore fiber, an anti-resonance hollow core optical fiber, and an optical fiber with D-shaped platform.

Photonic crystal fiber (PCF) or micro-structured optical fiber includes hollow channels running along the entire length of a glass strand, providing unique platform with long interaction length and engineerable dispersion for the studies of nonlinear optics, optical communication, optical/bio sensing, and so forth. The optical properties of PCFs can be changed by filling the hollow channels with materials such as semiconductors and metals to excite the Mie resonances and surface plasmon resonances. Those metal/semiconductor infiltrated fibers have been proposed to use for optical sensing and in-fiber device applications. Simplified version of photonic crystal fiber with enhanced light-matter interaction could be achieved by introducing a nanoscale hollow channel into conventional optical fiber (e.g., nanobore optical fiber). Such nanobore fiber further allows the light coupling to the plasmonic modes of gold nanowire for polarization conversion and optical detection of virus in nano-fluid channel.

The disclosure provides information to show the ENZ mode excitation in optical fiber platform and demonstrate that propagating fields can be confined inside a region coated with ENZ conducting oxide material that is incorporated into a nanostructured optical fiber waveguide. The novel hybrid optical fibers could be used as a platform for highly sensitive optical sensing and magneto/nonlinear-ENZ optical studies.

FIG. 1A is schematic of an example of an embodiment of an ENZ optical fiber waveguide design with two inserts of expanded cross sections of portions of a core with an ENZ coating and without an ENZ coating as indicated. The right insert (labelled Section (I)) of the structure is the hollow nanobore fiber. The left insert (labelled Section (II)) depicts the ENZ fiber where the inner surface of the central hollow channel is coated with layer of transparent conducting oxide (TCO) such as indium tin oxide (ITO). One example of an ENZ fiber 2 waveguide design is a modified version of nanobore fiber that includes three concentric cylindrical layers shown in FIG. 1A. The two outermost longitudinal layers act as cladding 4 and core 6, respectively. In this embodiment, the core contains a longitudinal nano-sized hollow channel 8 (also referenced herein as a “nanobore”), generally centrally located in the core. The cladding 4 can be for example a silica cladding, the core 6 can be for example a GeO2 wt. 9% doped silica core of 4 μm diameter, and the hollow channel 8 can be for example 200 nm in diameter. The sizes, thicknesses, and shapes can vary and are only an example for illustration. The innermost thin layer 10 is longitudinally formed from a film is made of ENZ material parallel to the core that in this embodiment surrounds the hollow channel 8 at least a portion of the length of the hollow channel. The subwavelength thickness of the ENZ layer ensures that the guided core fiber mode can be coupled to the thin film ENZ mode whose domain of existence is limited to film thickness much less than the plasma wavelength of the material at which its permittivity vanishes.

FIG. 1A′ is a schematic graph of transmission of a light through the optical fiber of FIG. 1A, based on wavelength. The ability to confine electromagnetic energy in a small space at the medium's ENZ wavelength motivates a search for highly confined propagating polariton modes using ENZ materials. Three-layer structures, where a sub-wavelength thin layer of indium tin oxide (ITO) is sandwiched between two dielectric layers, can support ENZ polariton modes. The disclosure shows the existence of a propagating mode in an optical fiber with a nano-hollow channel modified with an ENZ layer within which an enhanced field is excited.

Other TCO material, such as aluminum zinc oxide (AZO) and others, can be used for forming the thin film of the ENZ material. In some embodiments, other ENZ material, such as transition metal nitrides (TMNs) (e.g. titanium nitride (TiN) and zirconium nitride (ZrN)), can be used in addition to or in lieu of a TCO. In some nonlimiting examples of experiments disclosed and described herein, ITO, a CMOS compatible TCO material, is used as the ENZ medium in the analysis. The real part of ITO permittivity crosses zero at the bulk plasmon resonant wavelength, which can be tuned in near-infrared by controlling the carrier concentration of the material. The frequency dependent complex permittivity of ITO was calculated using the Drude model. For the designed ITO carrier concentration of 1021, the real part of permittivity function of the ITO crosses zero at 1068 nm and with small imaginary part of permittivity (lm(ε)=0.41). This carrier concentration of ITO could be achieved by various deposition techniques, for instance magneton sputtering and atomic layer deposition (ALD). ALD or wet chemistry techniques could be used to fabricate conducting oxide nano-layer inside the hollow channel of the fiber.

To understand the coupling mechanism between the guided mode in the nanobore fiber and the thin film ENZ mode, the effective index of the guided fundamental core mode of the nanobore fiber as a function of excitation wavelength was modelled using finite difference numerical waveguide analysis method (see Methods). The effective index of non-radiating thin film ENZ mode supported by the glass-ITO-air three-layer structure was modelled using the transfer matrix method (see Methods). The coupling between the fundamental mode of the nanobore fiber and thin film ENZ mode occurs at the phase matching wavelength, at which point the effective index functions of the two modes intersect and their momenta are equal. The results show that at the phase matching wavelength, the field confinement inside the ITO layer in the ENZ fiber is the highest and the mode has the highest loss, thus confirming the excitation of thin film ENZ mode in the fiber structure.

FIG. 1B is a schematic model of an example of an ENZ coating on a doped core surface for excitation of an NR-ENZ thin film mode. FIG. 1B′ is a schematic graph of absorption of a light through the model of FIG. 1B, based on wavelength. FIG. 1B shows an example of a glass-ITO-fluid three-layer structure 12 that is considered in calculating the thin film ENZ mode. The structure is comprised of a glass layer 14 corresponding to the core 6 in FIG. 1A, a thin ENZ layer 16 of, for example, ITO having the same thickness as the ENZ layer 10 inside the ENZ fiber 2 that is sandwiched between the glass layer 14 and a fluid layer 18 half spaces. In some embodiments, the fluid layer can be of air and in other embodiments, the fluid layer can be of other fluids such as the examples described below of ethanol and acetonitrile, and others that have different effects on the ENZ mode of the structure.

FIG. 2A is a schematic contour plot of reflectance as a function of wavelength and incident angle for a glass-ITO-ethanol as an example of a thin-film ENZ mode of a three-layer structure shown in the insert of FIG. 2D as in FIG. 1B (as a model of the Section (II) of FIG. 1A). FIG. 2B is a schematic contour plot of reflectance as a function of wavelength and incident angle for a glass-ITO-air as an example of a thin-film ENZ mode of a three-layer structure. FIG. 2C is a schematic contour plot of reflectance as a function of wavelength and incident angle for a glass-ITO-acetonitrile as an example of a thin-film ENZ mode of a three-layer structure. FIG. 2D is a schematic graph of field intensity (|E|) as a function of depth inside the ITO layer for the examples of structures in FIGS. 2A-2C, where a zero depth corresponds to the glass-ITO interface. The vertical white dashed lines are the light lines/critical angles; the curved white dotted lines are the ENZ dispersion curves; and the white crosses on the white dotted lines are the phase-matching angles/wavelengths.

To obtain the dispersion curve of the thin film ENZ mode, we investigated the glass-ITO-air three layer geometry shown in FIG. 1B using the transfer matrix method. The dispersion of fundamental mode of the hollow nanobore fiber was obtained using finite difference numerical waveguide simulations on the cross-section of the nanobore fiber. To ensure the excitation of the non-radiative ENZ mode, the ENZ mode is excited from the glass half space using Kretschmann. The thickness of the ITO layer is 20 nm. The reflectance is calculated for varying incident angles and wavelengths for three exiting media: ethanol, air, and acetonitrile. Light incident from glass onto the ITO layer is perfectly absorbed at angles larger than the critical angle and at resonant wavelengths that corresponds to the ENZ mode. A frequency dependent real part of the effective index of the mode n_(eff) was calculated (n_(eff)=cβ/ω, where β is the propagation constant in the fiber for a given wavelength). Contour plots of the reflectance as a function of incident angle and excitation wavelength is presented in FIGS. 2A, 2B, and 2C, respectively for ethanol, air, and acetonitrile as exiting media. For small enough thickness of ITO layer (d<λ/50), light incident from glass onto ITO nanolayer is perfectly absorbed at large angles and at resonant wavelength which corresponds to the ENZ polariton mode. Thus for each incident angle, the wavelength that corresponds to minimum reflectance is traced to calculate the effective index of the thin film ENZ mode (see FIGS. 2A-2C). The electric field profile across the ITO layer and the three exiting medium at the phase matching wavelength and angle is also calculated using transfer matrix simulations and shown in FIG. 2D.

FIG. 3 is a schematic graph of phase matching conditions between fundamental waveguide modes in a hollow nanobore fiber and thin-film NR-ENZ modes of a glass-ITO-air three-layer geometry with examples of ITO layer thicknesses of 5 nm, 10 nm, 15 nm, and 20 nm. The dotted curves are effective refractive indices of waveguide and thin-film modes as a function of wavelength. The solid curves and color-shaded areas are modal loss spectra of the fundamental mode excited in the ENZ fiber for the four ITO shell thicknesses described above.

To understand the phase matching condition, the effective index of the thin film ENZ modes for four different ITO layer thicknesses and the fundamental mode of hollow nanobore fiber were calculated and depicted in FIG. 3 . The thin film ENZ dispersion curves for the four thicknesses were calculated to show that the phase matching condition with fiber fundamental core modes depends on the thickness of the ITO layer. As the ITO thickness increases, the thin film ENZ dispersion curve shifts toward longer wavelengths and thus the phase matching wavelength (crossing wavelength) with the fiber fundamental core mode. The thin film dispersion curves intersect the fiber fundamental core mode dispersion at 1070 nm, 1079 nm, 1088 nm, and 1098 nm wavelengths for 5 nm, 10 nm, 15 nm, and 20 nm ITO layer thicknesses, respectively. Thus, in the ENZ fiber, the ENZ mode is expected to be excited at higher wavelengths for thicker ITO layers.

The excitation of ENZ modes in the fiber at the above resonant wavelengths was also verified. A finite difference method was used to solve the Maxwell's equations on a cross-section of the ENZ fiber waveguide. The resulted fundamental mode has highest spatial field distribution within the ITO layer compared to higher order modes. This ENZ mode was tracked over a wavelength range to calculate the modal loss:

loss=−20 log₁₀ e ^(−2πk/λ) ⁰ , where k is the imaginary part of the effective index).

The modal loss curves were calculated in the same way for four different ITO layer thicknesses: 5 nm, 10 nm, 15 nm, and 20 nm. FIG. 3 shows the modal losses of the fundamental mode of the ENZ fiber for four ITO layer thicknesses (color-shaded areas). Peak losses are observed at wavelengths 1071 nm, 1080 nm, 1092 nm, and 1102 nm for ITO layer thickness 5 nm, 10 nm, 15 nm, and 20 nm respectively. These resonances are in good agreement with the phase matching wavelengths of the nanobore fiber mode and the thin film ENZ modes calculated above. The peak in the loss spectra results from the excitation of ENZ thin film mode and the strong confinement/absorption by the ITO nanolayer.

The slight discrepancy between the phase matching and the peak loss wavelengths can be attributed to the mismatch between the excitation light sources: plane wave in the case of three layer geometry and core guided Eigen-mode source in the nanobore fiber. Another contributing factor is the curvature of the ITO layer inside the fiber that is cylindrical in contrast to the flat geometry of three-layer structure that is assumed when calculating the thin film ENZ modes. The resonance discrepancy is greater with increasing layer thickness due to the mismatch in the two geometries.

To study the nature of ENZ mode in the fiber, we plot the spatial electric field distributions of the fundamental mode supported by the ENZ fiber with 10 nm thick ITO layer at the ENZ wavelength and off-ENZ wavelength. FIG. 4A is a schematic electric field profile of the fundamental mode supported by the ENZ optical fiber at a 900 nm outside ENZ wavelength, the profile being across the entire fiber cross section in the top image with a zoomed schematic view of the core below the top image. The black circles outline the structure of the fiber. The figures shown are slightly elongated to fit the allowable margins and still show clarity. FIG. 4B is a schematic electric field profile of the fundamental mode supported by the ENZ optical fiber at a 1080 nm outside ENZ wavelength, the profile being across the entire fiber cross section in the top image with a zoomed schematic view of the core below the top image. FIG. 4C is a schematic electric field profile of the fundamental mode supported by the ENZ optical fiber at a 1300 nm outside ENZ wavelength, the profile being across the entire fiber cross section in the top image with a zoomed schematic view of the core below the top image. FIG. 4D is a schematic graph of the electric field along the diameter of the fiber in FIG. 4A at the 900 nm outside ENZ wavelength. FIG. 4E is a schematic graph of the electric field along the diameter of the fiber in FIG. 4B at the 1000 nm outside ENZ wavelength. FIG. 4F is a schematic graph of the electric field along the diameter of the fiber in FIG. 4C at the 1300 nm outside ENZ wavelength. At 1080 nm, which is the ENZ mode phase matching wavelength for 10 nm thick ITO layer, the magnitude of electric field is highly confined inside ITO layer (ENZ region) as shown in FIGS. 4B and 4E. The high field confinement in the ENZ nano-layer results in the highest modal loss at this wavelength as seen in FIGS. 2A-2C in the yellow solid curve.

Referring briefly to FIG. 5 , FIG. 5 is a schematic graph of modal losses of ENZ fiber higher order modes. Loss vanishes as the mode approaches cutoff wavelength. The graph shows the higher order modes TM₀₁, TE₀₁, and HE₂₁ cut off well below the ENZ regime of the ITO layer. Thus, only the fundamental mode HE₁₁ exhibits ENZ mode confinement. The field distribution does not exhibit radial symmetry, because the excitation fiber fundamental core mode is linearly polarized (HE₁₁). The radially polarized higher order mode\s (TM₀₁) is not supported by the nanobore fiber at the high wavelength regime.

FIG. 6A is a schematic graph of a complex refractive index of ITO as a function of free space wavelength. At the crossover of real and imaginary parts of the index, the real part of permittivity vanishes. FIG. 6B is a schematic graph of permittivity of ITO as a function of free space wavelength. At the crossover of real and imaginary parts of the index, the real part of permittivity vanishes. At a shorter wavelength (900 nm), the refractive index of ITO resembles that of a dielectric with real part of value (n=1.022) falls between that of air at the center and doped silica core (n=1.459). In this regime, the field distribution resembles the profile of the fundamental mode of hollow nanobore fiber as can be observed in FIG. 4A and FIG. 4D. At longer wavelength (1300 nm), ITO is in essence metallic-like having negative real part of permittivity (ε=—1.707+0.732i) with real part of index (0.274) smaller than imaginary part (1.335). Thus, the field is mostly contained in the core and central air channel, decaying inside the ITO layer as depicted in FIGS. 4C and 4F.

FIG. 7A is a schematic graph of refractive index dependence of the ENZ fiber based on various analytes placed inside the core channel of the fiber. The graph plots the loss spectra of ENZ mode for five analytes whose refractive indices at the resonant wavelengths are given within the parentheses. FIG. 7B is a schematic graph of a refractive index dependence of ENZ resonance wavelength. FIG. 7C is a schematic graph of a refractive index dependence of loss. The red lines are the linear fits to the data points obtained from the main graph of FIG. 7A and yield a slope of 121 nm/RIU. The field enhancement in the thin ITO layer suggests that the modal properties of the fiber ENZ mode may be sensitive to the perturbations of the surrounding medium's optical properties, in particular, the dielectric permittivity of the constituents in the central hollow channel. Thus, we investigated the dependence of the modal loss spectrum on the refractive index of the central channel. The fiber ENZ modal loss spectra calculated for five different fluids placed in the central channel of the fiber is depicted in FIG. 7A. The refractive index of the fluid at the resonant wavelength was stated inside the parentheses next to the name of the fluid. The permittivity functions of the fluids are obtained from other reports. The thickness of the ITO layer was kept at 20 nm. As seen in the figure, the resonant wavelength shifts from 1102 nm for air to 1156 nm for chloroform. The modal loss for chloroform is found to be 679 dB/cm, which is almost five times greater than with air at the central channel. Increasing the refractive index of the central region in the nanobore fiber effectively shifts the dispersion curve of both the guided fiber fundamental core mode and planar thin film ENZ mode (see FIGS. 2A-2C). This in turn results in the phase matching wavelength getting larger due to the change of the index of the hollow channel.

FIG. 8A is a schematic electric field profile at ENZ resonance for air as an analyte placed inside the core of an ENZ optical fiber with an ITO shell in the core, the profile being across the entire fiber cross section in the top image with an expanded schematic view of the core below the top image. The black circles outline the structure of the fiber. FIG. 8B is a schematic electric field profile at ENZ resonance for chloroform as an analyte placed inside the core of an ENZ optical fiber with an ITO shell in the core, the profile being across the entire fiber cross section in the top image with an expanded schematic view of the core below the top image. FIG. 8C is a schematic graph of the electric field along the diameter of the fiber in FIG. 8A. FIG. 8D is a schematic graph of the electric field along the diameter of the fiber in FIG. 8B.

FIGS. 8A-8D shows the comparison between the ENZ mode profiles for air and chloroform at the center of the ENZ fiber. Similar to the analysis in the planar structures, the field confinement of the ENZ mode is stronger with the external medium of chloroform, and thus the larger absorption of light was observed in the ENZ fiber with higher refractive index in the central nano-channel. A similar trend is observed in the field profiles for the three-layer geometry shown in FIG. 2D.

The strong dependency on the surrounding dielectric can be exploited for novel optical/bio sensing purposes due to the unique feature of the enhanced field confinement of the ENZ mode in the fiber. For wavelength-based sensing, the average refractive index sensitivity of the ENZ fiber, defined as AA/AN where N is the refractive index of the material in the central channel of the fiber is found to be 121 nm/RIU. The observed sensitivity is comparable with other in-fiber sensing device such as Mach—Zehnder interferometer with waist-enlarged fusion bitaper and it has better performance than some grating-based sensors. In addition, this type of ENZ fiber sensor could be used for sensing material with wide range of refractive index, including refractive index between 1.3-1.4 in which most of the biomaterial lie on. The sensitivity of the ENZ fiber could be significantly enhanced by optimizing the materials and geometry, such as ITO thickness, core/hole diameters, choices of ENZ materials, and the fundamental core mode dispersion (e.g. engineered dispersion with additional cladding holes).

Epsilon-Near-Zero and Field-Effect Tunable Properties in TCO/TMN

FIG. 9A is a schematic diagram of an example of a conducting oxide field-effect structure used in light manipulation. FIG. 9B is a schematic graph of a spatial distribution of the carrier concentration N for different applied voltages using the structure of FIG. 9A. FIG. 9C is a schematic graph of a corresponding real part of the dielectric permittivity of ITO at wavelength of 1550 nm. As referenced above, ENZ materials enable unique optical functions such as tunnelling of electromagnetic waves, non-reciprocal magneto-optical effects, and abnormal non-linearity, and include materials with low permittivity. Unique properties observed include enhanced absorption in TCO ENZ layers, advanced resonant coupling properties with antenna, and strongly enhanced nonlinear response and light generation in a TCO slab. A MOS-field effect ENZ structure 20 can be formed to gate the TCO/TMN materials by combining one or more ENZ layers 10, such as TCO or TMN layers, dielectric insulator layer 24, and a metal layer 26 such as shown in FIG. 9A. A bias voltage from a bias voltage source 28 can be applied to the structure. The permittivity of the TCO (such as ITO) would reach to the ENZ region (−1<εr<1) via gate-biasing at an applied bias of 2-4 V shown in the gray highlighted area of FIG. 9C, thus leading to a large electric field enhancement generated in the accumulation layer of the ITO. The field effect modulated refractive index change (Δn=1.39 at wavelength of 800 nm) is at least two orders of magnitude higher than is seen for electro-optic modulation using the Kerr effect. Since the drift velocity of electrons to form the accumulation layer is fast (exceeds THz), with the small footprint and low capacitance of nano-devices, the modulation speed could easily exceed tens of GHz to few hundred GHz, which apply to most of the meta-devices discussed in this disclosure. The low power consumption and high-speed operation device performance are significantly important for many critical applications.

Several studies have been done to demonstrate efficient modulators in a TCO plasmonic waveguide or planar structure geometries and TCO metamaterials. Using the field-effect modulation disclosed herein, a plasmonic modulator with record high dynamic range (2.71 dB/pm) and low waveguide loss (˜0.45 dB/pm) and a tunable metasurface with 1T phase shift via the electrically-induced coupling of ENZ resonance can be created. The TCO field-effect dynamic opens up the possibility of ultra-compact amplitude and phase modulation that can apply this effect to develop efficient dynamic ENZ/metasurface in-fiber devices.

Nanobore ENZ Optical Fiber

FIG. 10A is a schematic diagram of an example of a nanobore fiber used for excitation of ENZ resonance. FIG. 10B is a SEM image of a nanobore of the fiber of FIG. 10A showing an AZO coating in the hollow channel of the nanobore as an exemplary ENZ material. FIG. 100 is a schematic electric field profile of the fundamental mode supported by the ENZ optical fiber of FIG. 10A at a 900 nm outside ENZ wavelength. In at least one embodiment, the disclosed ENZ fiber 2 waveguide design can be a modified version of a nanobore fiber that includes three concentric cylindrical layers as shown in FIG. 1A and with more details on the core and hollow core in FIG. 10A. The two outermost layers act as cladding 4 at least partially around a core 6 (e.g., 4 μm diameter), and a hollow channel 8 of 200-500 nm diameter within the core as shown in FIG. 1A and FIG. 10A. The nanobore optical fiber transmits a large portion of the optical energy confined in the nanoscale central hollow channel in the guided core as shown in FIG. 100 .

Strong light-matter interaction with long interaction length (>10 cm) could be achieved when the hollow channel is filled with the targeted material. For example and without limitation, a 5-20 nm thin layer of TCO (e.g. ITO or AZO) using ALD can be deposited onto the central hollow channel of the fiber. Similar to a planar glass-ITO-air three-layer structure, the TCO material can support the ENZ mode at the wavelength the material's permittivity vanishes and induce strong absorption due to the excitation of ENZ polariton mode. A simulation in FIG. 100 shows that coupling between the fundamental mode of the nanobore fiber and thin film ENZ mode (ENZ wavelength at 1068 nm) (planar ENZ mode dispersion was calculated using transfer matrix method) can occur at the phase matching wavelength (the crossing point between the effective indexes of fundamental core mode and ENZ modes), resulting a loss peak in transmission (FIG. 4 ). In addition, as the ITO thickness increases, the thin film ENZ dispersion curve shifts toward longer wavelengths and thus the phase matching wavelength (crossing wavelength) with the fiber fundamental core mode.

Furthermore, at the phase matching wavelength, the field confinement inside the ITO layer in the ENZ fiber is the highest and the mode has the highest loss, thus confirming the excitation of the thin film ENZ mode in the fiber structure as described above and shown in FIG. 4B and FIG. 4E. Initial ALD fabrications confirm that AZO thin layer (<100 nm thick) could be fabricated on the hollow channel (500 nm diameter) of the nanobore fiber shown in FIG. 10B with length of ˜15 cm.

Anti-Resonance ENZ Hollow Core Fiber

FIG. 11A is a schematic diagram image of an example of another embodiment of an ENZ hollow core fiber with thin tubes around the periphery of a hollow core, the fiber having anti-resonance properties. FIG. 11B is a schematic enlarged diagram of the hollow core of the anti-resonance ENZ hollow core fiber in FIG. 11A. The anti-resonance ENZ fiber can include, for example, six uncoated thin tubes 30 with diameter of 12 μm and a hollow-core 8′ with a diameter of 26 μm. The anti-resonance hollow core optical fiber can also be used to excite the conducting oxide ENZ resonance.

FIG. 11C is a SEM of an example of TCO (AZO) nanoparticles deposited into the hollow core 8′. A similar ALD technique can be used to coat a nano-layer of TCO/TMN materials in the sidewall of the hollow core channel to form the ENZ layer. In addition, a wet chemistry technique can be used to synthesize AZO nanoparticles as a layer on the side wall. The AZO nanoparticles provide an extra degree of freedom to control the ENZ layer thickness and ENZ wavelength of the materials. AZO nanoparticles can be prepared with zinc acetate dehydrate Zn(CH3COO)2.2H2O as zinc precursor and Al-chloride AlCl3 as aluminum precursors. By changing the weight percentage of aluminum in zinc oxide, the aluminum doping concentration can be modified in ZnO routinely. The AZO nanoparticles are for example a diameter of 50-80 nm.

FIG. 11D is a schematic graph of measured transmission spectra for the anti-resonance fiber filled with the AZO nanoparticles with different doping concentrations. Preliminary results on the transmission measurements of AZO-filled anti-resonance fibers show a transmission dip in the near-IR regime. The transmission dip results from the coupling of the fundamental core mode to the AZO ENZ resonance. It also appears that the resonance dip shifts to a shorter wavelength with a higher doping concentration of the nanoparticles (more metallic). The results indicate the excitation of AZO ENZ resonance and could be useful for novel in-fiber applications to be discussed in the following section.

FIG. 11E is a schematic diagram of a hollow core photonic crystal fiber as an example of tubes outside the hollow core that can be used for anti-resonance properties. FIG. 11F is a schematic enlarged diagram of the hollow core with the surrounding tubes of the ENZ hollow core photonic crystal fiber in FIG. 11E. In like fashion described for the above embodiment in FIG. 11A, an ENZ layer of nanoparticles can be created in the hollow core 8′ to affect the responsive wavelengths of the fiber.

D-Shaped ENZ Optical Fiber

FIG. 12A is a schematic diagram of another embodiment of an ENZ fiber 2 having an ENZ layer 10 external to the core 6. The ENZ layer 10 can be, for example, a thin layer of TCO deposited using ALD and sputtering techniques on a surface 34 of the fiber 2. The ENZ layer can be formed in operational proximity to the core (generally external to the core), so that the ENZ layer can affect a light source passing through the core. The ENZ layer can be used for efficient excitation of an ENZ resonance. In at least one embodiment, the surface 34 can be formed as a flat platform to form a D-shaped cross section fiber. The flat platform of the D-shaped fiber can be fabricated by etching/polishing out the cladding, providing a smooth platform for ENZ material deposition. For example, the flat platform can be ˜1 μm apart from the doped core, resulting in a large evanescent field from the core to surround to the D-shaped cladding.

FIG. 12B is a schematic graph of a real part of permittivity dispersion of deposited AZO thin film with an ENZ wavelength of about 1580 nm. FIG. 12C is a schematic graph of a measured transmission spectrum of AZO ENZ materials on the ENZ fiber of FIG. 12A. Similar to the phase-matching coupling mentioned above, at the anti-crossing, the fundamental core mode can strongly couple with the ENZ mode of the nano-layer and cause the modal loss peak in the core. A preliminary experiment by depositing a 20 nm AZO ENZ thin film (ENZ wavelength ˜1400 nm) on the D-shape platform shows a strong resonance dip in the transmission in the AZO fiber with 1 cm of the D-shape region, caused by the ENZ mode resonance, shown in FIG. 12C. The resonance dip is strongest with the TM light excitation (vertical electrical field polarization), indicating the ENZ mode properties.

FIG. 12D is a schematic diagram showing a mode profile of the ENZ fiber of FIG. 12A at a resonance wavelength. FIG. 12E is a schematic diagram showing an enlarged y-component of electrical field distribution for TE incident light for the ENZ fiber of FIG. 12A. FIG. 12F is a schematic diagram showing an enlarged y-component of electrical field distribution for TM incident light for the ENZ fiber of FIG. 12A. FIG. 12G is a schematic diagram showing a line profile of the y-component electrical field distribution along a diameter of the ENZ fiber of FIG. 12A with TM incident light at a resonance wavelength. At the resonance wavelength, the electric field is strongly confirmed in the ENZ layer for the TM polarization state.

The above discussion provides information on the resonant coupling between the propagating fiber fundamental core mode and ENZ mode in an ENZ meta-optical fiber. The results suggest that ENZ optical fiber will find advantages for enhanced light-matter interaction with long interaction length for studying novel ENZ optical properties and in-fiber ENZ device applications. More advanced properties of the ENZ meta-fibers will be discussed in the following section.

Enhanced Magneto-Optical Faraday Rotation in ENZ Fiber for Optical Isolation.

Magneto-optical (MO) Faraday rotation has been studied extensively in MO-active materials such as yttrium iron garnet crystals for the application of optical isolation. In such components, optical isolation is achieved by altering the propagation of light by application of an external magnetic field. The magnitude of the Faraday Effect is governed by the Verdet constant, VB, which is a characteristic property of the material. Since the degree of Faraday rotation depends on the product of the Verdet constant and the optical path-length, materials with a smaller Verdet constant require a longer path-length for complete optical isolation. However, typical optical materials (e.g. SiO2 glass) has small Verdet constant. Integration of plasmonic and metamaterial structures with ferromagnetic materials have been proposed to enhance the interaction and the Verdet constant of the nanostructures, including metallic hole-array/slit, nano-plasmonic disk/ring, multilayer structures, and propagating plasmonic structure. However, those magneto-plasmonic structures typically exhibit a high optical losses and Faraday rotation with more than 20 degrees is virtually unachievable.

The zero-index materials and metafilm show promise for non-reciprocal magneto-optical enhancement. Since the Faraday rotation

${{\Delta\theta} \propto \frac{\varepsilon_{xy}}{n}},$

where me ε_(x,y) is off-diagonal component of the permittivity tensor of the materials and n is the linear refractive index of the material, strong MO-enhancement could be observed when the linear refractive index reached close to zero (ENZ regime). However, to date, there is no experimental verification on the enhanced Faraday rotation in ENZ materials due to the weak interaction from the ultra-thin ENZ films or metasurfaces.

It is believed that the non-reciprocal magneto-optical effects of ENZ materials can be demonstrated and verified by integrating the ENZ active layer into the ENZ optical fiber with long interaction length. The result can be a MO-ENZ fiber with large Faraday rotation of >90 degrees. In addition, the result can be a reconfigurable TCO nanostructures that provide field-effect tuning of the magneto-optical response in ENZ fiber for development of novel in-fiber isolator and modulator.

FIG. 13A is a schematic diagram of another embodiment of an ENZ fiber having an ENZ layer with magneto-optical (MO) properties. FIG. 13B is a schematic diagram of polarized input light being reoriented by magnetic field through the ENZ coating in the ENZ fiber of FIG. 13A. The ENZ fiber 2, as described above in FIG. 1A, can have a cladding layer 4 with an internal core 6 having a hollow channel 8. The ENZ layer 10 can be formed in the hollow channel 8. The MO Faraday rotation for nanobore ENZ fiber, anti-resonance hollow core ENZ fiber, and D-shaped ENZ fiber discussed above can be shown by measuring the change of polarization state with the applied magnetic field FIG. 13B.

FIG. 13C is an example of a system to reorient and measure a polarized light through the ENZ fiber of FIG. 13A. The system 40 can include a light source 42, such as a broadband super continuum (SC) light source, light filter 44, such as a bandpass filter or monochromator, polarizer 46, objective 48, magnetic field source 50, such as a pulsed magnetic coil (up to few hundred mT), and high-sensitivity polarimeter 52 and can be used in the MO measurements. In one example, to minimize the size of the device, the fiber can be coiled multiple turns at several millimeters in diameter. A permanent magnet with magnetic field up to 1-2 T can be used for small polarization rotation. The differences of the polarization angle and the ellipticity between the on- and off-states can be taken to calculate a Faraday rotation angle θ_(F). The wavelength dependent Faraday rotation angle can also be measured particularly near the ENZ resonance wavelength for the proposed ENZ fibers described herein.

Results can also account for the effective Verdet constant

${V = \frac{\theta_{F}}{lB}},$

where the l is the length of the fiber and B is the applied magnetic field. Enhanced Faraday rotation exists in tellurite glass (77TeO2-20ZnO-2.5La2O3) filled optical fiber. Wavelength dependence of effective Verdet constant of the fundamental core mode of the hybrid waveguide with ˜2-15 rad/mT can be observed (two order of magnitude higher than silica fiber). The same technique can be used for measuring the Verdet constant of the ENZ fiber. It is believed that a strong enhancement of magneto-optical effects at the ENZ resonance exist for development of efficient a compact in-fiber optical isolator.

Light Modulation in Optical Fiber

FIG. 14A is a schematic diagram of another embodiment of an ENZ fiber having a tunable ENZ coating external to the core. Light modulation in the optical ENZ fiber can be further demonstrated by using an example of a MOS field-effect structure, such as described in FIG. 9A. This structure can include, for example, an ENZ fiber 2, for example a D-shaped fiber, cladding 4, core 6, ENZ layer ITO layer 10, dielectric layer 24, such as a thin HfO2 layer, and metal layer 26, such as a gold layer. By applying bias from a bias voltage source 28 between the gold and thin ITO layer, the carrier concentration and permittivity of active layer of ITO near the HfO2-ITO interface can be tuned, thereby changing the coupling of the ENZ fundamental core mode and allowing modulation of light in the fiber such as shown in FIG. 9B and FIG. 9C. For example, such modulation can provide tunable MO-effects and enhanced light emission of ENZ optical fibers for active magneto-optical responses and amplitude modulation.

FIG. 14B is a schematic graph of a change of the loss from 0V to 5V for various wavelengths of the ENZ fiber of FIG. 14A. Our preliminary simulation combined with electrostatic and electromagnetic modelling shows that a change of loss peak for ˜3.7 dB/cm could be achieved by applying 5 V.

FIG. 14C is a schematic diagram of a carrier concentration profile of the ITO layer for the ENZ fiber of FIG. 14A without an applied voltage. FIG. 14D is a schematic diagram of a carrier concentration profile of the ITO layer for the ENZ fiber of FIG. 14A with an applied voltage of 3 V. The ENZ field profile changes significantly due to the applied bias. The coupling of the ENZ mode and the modulation strength can be further enhanced by reducing the separation between the core of fiber and the ENZ layer, and the thickness of the ENZ layer. The strong change of the ENZ mode coupling can induce a significant change of the quantum emission and MO ENZ effects and provide an active manipulation of light emission, polarization, and amplitude in ENZ optical fiber with ultrafast response and low energy consumption.

A tunable ENZ optical fiber is significant because it can provide with the coupling of the ENZ fiber mode for enhancing and manipulating the magneto-optical effects and light emission. Such enhancements can include, for example, a novel ENZ meta-fiber optical isolator, modulator, and an efficient specialty optical fiber laser.

In summary, the above description shows the ENZ modes supported by a hollow fiber waveguide modified with a thin conducting oxide layer in some embodiments or an ENZ layer external to the core, each that are capable of confining high intensity fields inside a subwavelength cross-sectionally dimensioned nano-channel. At the dielectric to metal crossover point of the conducting oxide, the permittivity approaches zero enabling the excitation of ENZ mode characterized by high field enhancement in the ENZ region. The sensitivity of the waveguide's modal loss to the central channel refractive index can be exploited to sense refractive index of medium and therefore the ENZ fiber has potential applications in many applications including such as optical/bio-sensing. In addition, due to the excitation of the highly confined ENZ mode in the optical fiber waveguide, the ENZ fiber could be potentially useful in studying nonlinear and magneto-optics as well as enhanced quantum emission near ENZ medium, and transmitting optical energy below the diffraction limits in fiber.

Methods

Numerical simulations of the waveguide structure were carried out using the MODE Solutions software from Lumerical Solutions, Inc. The effective index of the ENZ mode supported by three layer structures was calculated using of a MATLAB code developed by G. Figliozzi and F. Michelotti at the University of Rome “La Sapienza” (Italy) based on the transfer matrix method. In the simulations, permittivity function of silica is modelled using the Palik data. Permittivity of GeO2 doped silica (GeO2 wt. 9% doped silica) is obtained from the literature. For ITO, the Drude model is used with the parameters: the electron concentration of 1.0×1021 cm⁻³, ε^(∞)=3.6, Γ=2.0263×1014 s⁻¹, ωp=3.3722×1015 s⁻¹, In the index sensing analysis, the permittivity functions of the liquids that are placed inside central channel to be analyzed are obtained from literature.

Other and further embodiments utilizing one or more aspects of the inventions described above can be devised without departing from the disclosed invention as defined in the claims. For example, other embodiments can include other shapes and types of optical fibers, other ENZ materials for forming a film on or in an optical fiber, other MOS structures and materials, other thicknesses and frequencies, and other variations than those specifically disclosed above within the scope of the claims.

The invention has been described in the context of preferred and other embodiments and not every embodiment of the invention has been described. Obvious modifications and alterations to the described embodiments are available to those of ordinary skill in the art. The disclosed and undisclosed embodiments are not intended to limit or restrict the scope or applicability of the invention conceived of by the Applicant, but rather, in conformity with the patent laws, Applicant intends to protect fully all such modifications and improvements that come within the scope or range of equivalents of the following claims. 

1. An optical fiber, comprising: a longitudinal core layer of dielectric material; a longitudinal cladding layer surrounding at least a portion of the core; and a longitudinal layer of ENZ material formed parallel to the core, wherein the ENZ layer is configured to change a rotational angle of incoming light with an applied magnetic field.
 2. The optical fiber of claim 1, wherein the core comprises a hollow channel having a subwavelength cross sectional dimension and the ENZ layer is formed in the hollow channel.
 3. The optical fiber of claim 2, wherein the ENZ layer is formed of ENZ particles.
 4. The optical fiber of claim 2, wherein a fluid is supplied to hollow channel and configured to change the ENZ layer performance.
 5. The optical fiber of claim 1, wherein the ENZ layer is formed in operational proximity to the core and configured to affect a light passing through the core.
 6. The optical fiber of claim 5, wherein the ENZ layer is formed external to the core on a planar surface of the cladding layer.
 7. The optical fiber of claim 1, wherein the ENZ layer comprises at least one of a transparent conducting oxide or a transition metal nitride formed on a planar surface of the cladding layer external to the core and parallel to the core.
 8. The optical fiber of claim 1, further comprising a dielectric layer coupled to the ENZ layer, and a metal layer coupled to the dielectric layer.
 9. The optical fiber of claim 1, further comprising a bias voltage source coupled to the metal layer and the ENZ layer.
 10. An optical fiber, comprising: a longitudinal hollow core; a longitudinal cladding layer surrounding at least a portion of the core; and a longitudinal layer of ENZ material formed parallel to the core, wherein the ENZ layer is configured to change a rotational angle of incoming light with an applied magnetic field. 11-18. (canceled)
 21. An optical fiber, comprising: a longitudinal core layer of dielectric material; a longitudinal cladding layer surrounding at least a portion of the core; and a longitudinal layer of ENZ material of at least one of transparent conducting oxide or a transition metal nitride formed parallel to the core, wherein the ENZ layer is configured to change a rotational angle of input light relative to orthogonal axes transverse to the longitudinal core with an applied magnetic field to produce a rotated output light compared to the input light.
 22. The optical fiber of claim 7, wherein the incoming light comprises polarized light.
 23. An optical fiber, comprising: a longitudinal core layer of dielectric material; a longitudinal cladding layer surrounding at least a portion of the core; and a longitudinal layer of ENZ material of at least one of a transparent conducting oxide or a transition metal nitride formed in operational proximity to the core and configured to affect light passing through the core, wherein the ENZ layer is configured to change a rotational angle of the light with an applied magnetic field. 